Can I make Ammonium Chloride + Water into a Gel?


Doodah

Recommended Posts

Hello all,

(Sorry if I've posted this in the wrong section)
I have a question for all you clever souls out there!

I'm doing some chemical woodburning, using a mix of ammonium chloride and water, then applying a small amount over a stencil vinyl, peeling it off and then using a heat gun to burn the design into the wood.
I am having a problem with the solution soaking into the grain instantly and therefore bleeding.
I've tried a reverse stencil, spraying varnish then peeling off the stencil and using the solution on the bare areas, but it's still soaking into the grain and blurring the design.

So I'm thinking, how about if I can thicken the solution to a gel like consistency? (Like how you can use a gel wood stain which helps to prevent bleeding with stencils)

Does anyone know what would be the best way to go about this, would gelatin work? Or would some other thickening agent work better?

Any help greatly appreciated!!

Thanks, Becky

Edited by Doodah
Link to comment
Share on other sites

I found this method:

Quote

I cut a vinyl decal on a vinyl cutter. Applied it to wood. Painted with matte clear coat. Rustoleum 2X spray paint. Removed decal. Let dry. Apply the ammonium chloride solution. Heat gun as usual. Done. End result, is perfect. NO bleeding, or discoloration. Just a perfect result. 

https://makezine.com/projects/make-35/chemical-woodburning/  

The clear coat is thicker, so it wont bleed under the vinyl, then when the vinyl's removed, the clear coat won't allow the chloride to bleed passed the clear coat. You just might have to reverse how you make your stencil, whether it's a positive or a negative of your design. Seems like a workable solution. A rubber-faced  roller might be useful to make sure the stencil edges are stuck firmly before clear coating

32 minutes ago, Doodah said:

Hello all,

(Sorry if I've posted this in the wrong section)
I have a question for all you clever souls out there!

I'm doing some chemical woodburning, using a mix of ammonium chloride and water, then applying a small amount over a stencil vinyl, peeling it off and then using a heat gun to burn the design into the wood.
I am having a problem with the solution soaking into the grain instantly and therefore bleeding.
I've tried a reverse stencil, spraying varnish then peeling off the stencil and using the solution on the bare areas, but it's still soaking into the grain and blurring the design.

So I'm thinking, how about if I can thicken the solution to a gel like consistency? (Like how you can use a gel wood stain which helps to prevent bleeding with stencils)

Does anyone know what would be the best way to go about this, would gelatin work? Or would some other thickening agent work better?

Any help greatly appreciated!!

Thanks, Becky

 

Edited by StringJunky
Link to comment
Share on other sites

Hi, Thanks for the reply :)

I tried this method, I reversed the stencil and sprayed Plasti-Kote clear matt sealer over the area. I did about about 3 light coats but didn't leave much time between them. I let it dry, removed the stencil and painted on the ammonium solution and used the heat gun on it. It worked a bit better than without the spray coat but it's still bled. Maybe i'll try that method again, doing more coats and leave more time between them. I'll see if I can upload a couple of pics.

Edited by Doodah
Link to comment
Share on other sites

10 minutes ago, Doodah said:

Hi, Thanks for the reply :)

I tried this method, I reversed the stencil and sprayed Plasti-Kote clear matt sealer over the area. I did about about 3 light coats but didn't leave much time between them. I let it dry, removed the stencil and painted on the ammonium solution and used the heat gun on it. It worked a bit better than without the spray coat but it's still bled. Maybe i'll try that method again, doing more coats and leave more time between them. I'll see if I can upload a couple of pics.

Don't let the sealer spray droplets join up into a liquid film when you spray, as that is when it will run under the stencil. Do light sprays  and each time going for an orange peel effect. In a nutshell, you are spraying each layer too heavily so that it can run... go for a more powdery spray effect. When it's all done and dried properly you can smooth the orange peel effect with a light sanding action with the green side of a washing up sponge or one of those green plastic scouring pads to give a satin finish.

Edited by StringJunky
Link to comment
Share on other sites

It was a very fine misting when I applied it, I don't think the spray got under the stencil vinyl at all as when I peeled the vinyl off you could see the difference in the wood surface.

This is the stencil:
(and I reversed it for the spray sealer attempt)

36815004_10160490351945004_5855743499239948288_n.thumb.jpg.c06baea8bb595dfdedb367d6e5587fe9.jpg

 

This was the first attempt, applying the ammonium water solution straight onto it:

36871630_10160490351955004_4041178692091641856_n.thumb.jpg.01adf48d8e03d5de5b9ec7536f47a252.jpg

 

This was the 2nd attempt with the reversed stencil and spray sealer:

36823914_10160490351520004_8137102102489989120_n.thumb.jpg.c0d9b57397e62d9889fee515956f020b.jpg

Much better, but still bled and over time it's become more blurry now too.

Link to comment
Share on other sites

Ok thanks so much. The wood is just a test piece I'm using before applying this technique to my craft projects which are very smooth silver birch log slices, so I think it will work much better on them I reckon.
This test piece is just a length of kiln-dried, planed softwood timber cladding I got from a DIY store. (was only 69p)
I think I'll try again tomorrow and I'll sand the area really well first to make it super smooth and then apply the varnish again, but leave it to dry longer between the coats and see if that makes a difference.

Edited by Doodah
Link to comment
Share on other sites

4 minutes ago, Doodah said:

Ok thanks so much. The wood is just a test piece I'm using before applying this technique to my craft projects which are very smooth silver birch log slices, so I think it will work much better on them I reckon.
This test piece is just a length of softwood timber cladding I got from a DIY store.
I think I'll try again tomorrow and I'll sand the area really well first to make it super smooth and then apply the varnish again, but leave it to dry longer between the coats and see if that makes a difference.

Try that and post back.  Follow the grain when sanding, and with a block.

Edited by StringJunky
Link to comment
Share on other sites

Heya,
I've tried it again, this time waiting longer between the coats of spray and then leaving it overnight (say only takes an hour to full dry anyway)
I applied the solution now and quickly got the heat gun straight on it. 
Well the actual design looks brill and hardly any bleeding basically. But what it looks like to me is that the varnish is burning/the heat gun is burning through the varnish to the wood?

 

36805862_10160496193960004_2189033423614509056_n.jpg

Appears that if you get any of the solution on the varnished area then it's just going to burn through the varnish as well, so not sure how to get around that other than using a small brush and trying to paint each little area really carefully and try and not go outside the stencil area.

Edited by Doodah
Link to comment
Share on other sites

1 hour ago, Doodah said:

Heya,
I've tried it again, this time waiting longer between the coats of spray and then leaving it overnight (say only takes an hour to full dry anyway)
I applied the solution now and quickly got the heat gun straight on it. 
Well the actual design looks brill and hardly any bleeding basically. But what it looks like to me is that the varnish is burning/the heat gun is burning through the varnish to the wood?

 

36805862_10160496193960004_2189033423614509056_n.jpg

Appears that if you get any of the solution on the varnished area then it's just going to burn through the varnish as well, so not sure how to get around that other than using a small brush and trying to paint each little area really carefully and try and not go outside the stencil area.

At least you now know the source of the bleeding and that's a good result. Are you using the same lacquer as other people that do it?

Link to comment
Share on other sites

I'm not too sure what other people have used, one video they show they are using rustoleum enamel clear spray.
I'm about to try it again but I'm going to try paint the solution on more carefully and also maybe try a lower heat but take longer over the areas

 

Link to comment
Share on other sites

1 hour ago, Doodah said:

I'm not too sure what other people have used, one video they show they are using rustoleum enamel clear spray.
I'm about to try it again but I'm going to try paint the solution on more carefully and also maybe try a lower heat but take longer over the areas

 

If that fails, you can get high temperature clear lacquer if that's the problem. It's not too dear. Here's a  UK example:

https://www.amazon.co.uk/Tech-Xtremely-Temperature-LACQUER-Exhaust/dp/B00ZXZP480

I suspect the Rustoleum spray is more temperature tolerant than normal lacquers; it's got 'enamel' in its name.

Edited by StringJunky
Link to comment
Share on other sites

Yeah I was looking for something like that too, I was seeing if I could find a matt one (that one gives a satin sheen apparently) but it might still look ok anyway. I'm trying one more attempt now, on an actual wood slice I'll be using. I've just tried it on one already and turns out the stencil seems to leave some of it's adhesive on the silver birch, even after sanding it more. So now I'm going to try one more go - I'm spraying the whole thing in varnish, waiting 20 mins (Touch dry) spraying another coat, waiting 1 hour (full dry) and then applying the normal stencil over the top and applying the solution (this way it'll protect the solution from going where I don't want it). Then peel the stencil off and heat with gun and it should heat through the lacquer on those areas. Fingers Crossed! 

If that doesn't work I may have to try the high temp lacquer or just resort to using stain, paint, or ink, which I didn't really want to do but might be the only option to get a neat design.

Thanks for all your help and suggestions so far by the way! :)

Edited by Doodah
Link to comment
Share on other sites

You can fully matte the lacquer with a Scotchbrite pad when you are done and it's cured properly. I did that on my gloss guitar and it came out great. Just maintain one direction until it looks even then wipe with a damp cloth to clean it.

Link to comment
Share on other sites

Nope, spraying 2 coats and leaving it to fully dry and then applying stencil etc.. has not works at all. I applied the solution with the stencil on, lifted the stencil off and the solution had still soaked into the wood instantly, bleeding all under the stencil, even though it's been sealed!?! Perhaps the wood is just soaking in the sealer varnish too..?
So I don't have a clue, I thought the birch would be much easier than the test wood but it's proving to have much more of an issue..

Left side = reverse stencil, sealer, stencil off, apply solution, heat.
Right side = Sealer all over wood, apply normal stencil, apply solution, stencil off, heat.

36880729_10160497352325004_9039854483797966848_n.thumb.jpg.71d88ccfe64f074223ed78d34f849b8d.jpg

neither good results :(
 

Link to comment
Share on other sites

Oh dear. Have you watched this video. They show several different ways. The one showing where the liquid is put in a pen at 1.06 and using your stencil above looks right for you I think  and no need for lacquer. Note the stencil is stuck down in the vid, so you may need to do that each time.

 

Edited by StringJunky
Link to comment
Share on other sites

Ah yes that's the original video i watched to gave me the idea to do it. But seems no matter what I do it just wants to soak into the birch wood, even if I use a small amount on a tiny paintbrush. I think I may have to give up with it, I've tried 3 different ways on the wood slices and none worked. On the remaining blank side of one, I just decided to try using an ink pad and it came out really well. I need them to be neat and consistent with a stencil as Its for my etsy shop.
This is with pink and silver ink:

36832178_10160497455385004_4863097946347929600_n.thumb.jpg.4ee14ed6abea81aa8f133907f4595002.jpg

Link to comment
Share on other sites

11 minutes ago, Doodah said:

Ah yes that's the original video i watched to gave me the idea to do it. But seems no matter what I do it just wants to soak into the birch wood, even if I use a small amount on a tiny paintbrush. I think I may have to give up with it, I've tried 3 different ways on the wood slices and none worked. On the remaining blank side of one, I just decided to try using an ink pad and it came out really well. I need them to be neat and consistent with a stencil as Its for my etsy shop.
This is with pink and silver ink:

36832178_10160497455385004_4863097946347929600_n.thumb.jpg.4ee14ed6abea81aa8f133907f4595002.jpg

That's nice. Have you tried  stamping your design the same way and setup with the chloride solution?

Edited by StringJunky
Link to comment
Share on other sites

  • 2 years later...

 I joined so I could share my experience here. I have shared your problem and here is what has worked for me.

The first photo is 100ml water and a tablespoon ammonium chloride.

 

The second is 100ml water and 1 tablespoon cornstarch, microwaved for 90 seconds, with 100ml more water and 1 tablespoon ammonium chloride. My painting skills and patience with a heat gun need work but no bleed!

Hope it helps.

20200803_171403(1).jpg

20200803_171358(1)(1).jpg

Link to comment
Share on other sites

  • 6 months later...

I use a food thickener called ThickIt about 1 tbsp to 5-6 tsp of ammonium chloride and 1/2 cup warm water.  Stir and let it thicken about 2 minutes.  Brush on and let dry then remove stencil and use heat gun.  Works every time! Good luck! 

Link to comment
Share on other sites

I did my Apprenticeship with ICI of Australia and spent some time in the Chlorine production section. We detected Cl leaks by spraying Ammonia around joints etc. If there was a leak, a cloudy gas would form...Ammonium Chloride.

I also was gassed on one occasion, an experience that I would not want to go through again. 

Link to comment
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now
×
×
  • Create New...

Important Information

We have placed cookies on your device to help make this website better. You can adjust your cookie settings, otherwise we'll assume you're okay to continue.